2-D Electronic Materials: Epitaxial Growth Of Graphene On 6H-Silicon Carbide (0001)

Other Titles

Abstract

Graphene holds great promise as a material for high-speed electronics, especially as Si technology approaches its performance limits. Growth of epitaxial graphene by thermal decomposition of SiC is considered to be one of the most promising production routes since it has the potential to produce homogenous, wafer-size films directly on a semi-insulating or semiconducting substrate. Furthermore, graphene's planar 2-D structure enables devices and circuit designs with standard top-down lithography and processing techniques. However, the growth mechanism of graphene on SiC is not very well understood and much work remains to be done to improve the morphology, domain size and epitaxial quality of the grown graphene in order to take advantage of the unique properties of the material. This research work was aimed at using a modified CVD chamber in the Cornell University Wide-Bandgap-Semiconductor Laboratory to optimize the growth of epitaxial graphene by controlled decomposition of 6H-SiC(0001) in an argon mediated gas flow at near atmospheric pressure. Grown films were characterized using Raman spectroscopy, atomic force microscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, and electrical measurements. Uniform large-area monolayer and few-layer epitaxial graphene were successfully grown on SiC terraces of up to 8 [MICRO SIGN]m wide, and with Hall mobilities of up to 840 cm2/V.s. The as-grown graphene was found to be intrinsically electron doped with sheet carrier density in the range of 3 - 9 x 1012 cm-2. However, certain growth features that tended to disrupt growth by uniform step flow decomposition were observed. These included deep rounded pits at higher temperatures, shallow triangular pits, arrow-like incursions across terraces, finger growths, residual SiC islands on terraces, nucleation of graphene at multiple defect points on terraces, and extra graphene layers at step edges. Further research is required to determine the mechanisms of formation of these features and to determine how they can be eliminated or reduced. For the first time SiC grown epitaxial graphene films, transferred from the substrate by a special process, was imaged in plan-view by TEM. The TEM images, along with selected-area electron diffraction, showed that a bilayer film had the AB Bernal stacking. !

Journal / Series

Volume & Issue

Description

Sponsorship

Date Issued

2015-01-26

Publisher

Keywords

epitaxial graphene; 6H-silicon carbide

Location

Effective Date

Expiration Date

Sector

Employer

Union

Union Local

NAICS

Number of Workers

Committee Chair

Spencer, Michael G.

Committee Co-Chair

Committee Member

Van Dover, Robert B.
Thompson, Michael Olgar

Degree Discipline

Electrical Engineering

Degree Name

Ph. D., Electrical Engineering

Degree Level

Doctor of Philosophy

Related Version

Related DOI

Related To

Related Part

Based on Related Item

Has Other Format(s)

Part of Related Item

Related To

Related Publication(s)

Link(s) to Related Publication(s)

References

Link(s) to Reference(s)

Previously Published As

Government Document

ISBN

ISMN

ISSN

Other Identifiers

Rights

Rights URI

Types

dissertation or thesis

Accessibility Feature

Accessibility Hazard

Accessibility Summary

Link(s) to Catalog Record